本文所有数据均来自国家标准《GB/T1220—1992》，以示比较奥氏体不锈钢如国标304不锈钢，与新“200”系不锈钢，也就是马氏体不锈钢如202，201型不锈钢的成分区别，另请参考文章《镍在不锈钢中的作用》。供您参考。
奥氏体型
| 牌号 | 化学成分(质量分数)，% | ||||||||
| C(碳) | Si(硅) | Mn(锰) | P(磷) | S(硫) | Ni(镍) | Cr(铬) | Mo(钼) | 其他 | |
| 1Cr17Mn6Ni5N | ≤0.15 | ≤1.00 | 5.50～7.50 | ≤0.060 | ≤0.030 | 3.50～5.50 | 16.00～18.00 | — | N：≤0.25 |
| 1Cr18Mn8Ni5N | ≤0.15 | ≤1.00 | 7.50～10.00 | ≤0.060 | ≤0.030 | 4.00～6.00 | 17.00～19.00 | — | N：≤0.25 |
| 1Cr18Mn10Ni5Mo3N | ≤0.10 | ≤1.00 | 8.50～12.00 | ≤0.060 | ≤0.030 | 4.00～6.00 | 17.00～19.00 | 2.8～3.5 | N：0.20～0.30 |
| 1Cr17Ni7 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 6.00～8.00 | 16.00～18.00 | — | |
| 1Cr18Ni9（304） | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 8.00～10.00 | 17.00～19.00 | — | |
| Y1Cr18Ni9 | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.020 | ≥0.15 | 8.00～10.00 | 17.00～19.00 | ||
| Y1Cr18Ni9Se | ≤0.15 | ≤1.00 | ≤2.00 | ≤0.020 | ≤0.060 | 8.00～10.00 | 17.00～19.00 | — | Se：≥0.15 |
| 0Cr18Ni9 | ≤0.07 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 8.00～11.00 | 17.00～19.00 | — | |
| 00Cr19Ni10 | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 8.00～12.00 | 18.00～20.00 | — | |
| 0Cr19Ni9N | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 7.00～10.50 | 18.00～20.00 | — | N：0.10～0.25 |
| 0Cr19Ni10NbN | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 7.00～10.50 | 18.00～20.00 | — |
Nb：≤0.15 N：0.15～0.30 |
| 00Cr18Ni10N | ≤0.03 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 8.50～11.50 | 17.00～19.00 | — | N：0.12～0.22 |
| 1Cr18Ni12 | ≤0.12 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 10.50～13.00 | 17.00～19.00 | — | |
| 0Cr23Ni13 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 12.00～15.00 | 22.00～24.00 | — | |
| 0Cr25Ni20 | ≤0.08 | ≤1.00 | ≤2.00 | ≤0.035 | ≤0.030 | 19.00～22.00 | 24.00～26.00 | — | |
马氏体型
| 牌号 | 化学成分(质量分数)，% | ||||||||
| C(碳) | Si(硅) | Mn(锰) | P(磷) | S(硫) | Ni(镍) | Cr(铬) | Mo(钼) | V(钒) | |
| 1Cr12 | ≤0.15 | ≤0.50 | ≤1.00 | ≤0.035 | ≤0.030 | 11.50～13.090 | — | — | |
| 1Cr13 | ≤0.15 | ≤1.00 | ≤1.00 | ≤0.035 | ≤0.030 | 11.50～13.50 | — | ||
| 0Cr13 | ≤0.08 | ≤1.00 | ≤1.00 | ≤0.035 | ≤0.030 | 11.50～13.50 | 0.30～0.60 | — | |
| Y1Cr13 | ≤0.15 | ≤1.00 | ≤1.25 | ≤0.060 | ≥0.15 | 12.00～14.00 | — | — | |
| 1Cr13Mo（202） | 0.080～0.18 | ≤0.60 | ≤1.00 | ≤0.035 | ≤0.030 | 11.50～14.00 | — | — | |
| 2Cr13 | 0.16～0.25 | ≤1.00 | ≤1.00 | ≤0.035 | ≤0.030 | 12.00～14.00 | — | — | |
| 3Cr13 | 0.26～0.35 | ≤1.00 | ≤1.00 | ≤0.035 | ≤0.030 | 12.00～14.00 | — | — | |
| Y3Cr13 | 0.26～0.40 | ≤1.00 | ≤1.25 | ≤0.060 | ≥0.15 | 12.00～14.00 | — | ||
| 3Cr13Mo | 0.28～0.35 | ≤0.80 | ≤1.00 | ≤0.035 | ≤0.030 | 12.00～14.00 | 0.50～1.00 | — | |
| 4Cr13 | 0.36～0.45 | ≤0.60 | ≤0.80 | ≤0.035 | ≤0.030 | 12.00～14.00 | — | — | |
| 1Cr17Ni2 | 0.11～0.17 | ≤0.80 | ≤0.80 | ≤0.035 | ≤0.030 | 1.50～2.50 | 16.00～18.00 | — | — |
| 7Cr17 | 0.60～0.75 | ≤1.00 | ≤1.00 | ≤0.035 | ≤0.030 | 16.00～18.00 | — | ||
| 8Cr17 | 0.75～0.95 | ≤1.00 | ≤1.00 | ≤0.035 | ≤0.030 | 16.00～18.00 | — | ||
| 9Cr18 | 0.90～1.00 | ≤0.80 | ≤0.80 | ≤0.035 | ≤0.030 | 17.00～19.00 | — | ||
| 11Cr17 | 0.95～1.20 | ≤1.00 | ≤1.00 | ≤0.035 | ≤0.030 | 16.00～18.00 | — | ||
| Y11Cr17 | 0.95～1.20 | ≤1.00 | ≤1.25 | ≤0.060 | ≥0.19 | 16.00～18.00 | — | ||
| 9Cr18Mo | 0.95～1.10 | ≤0.80 | ≤0.80 | ≤0.035 | ≤0.030 | 16.00～18.00 | 0.40～0.70 | — | |
| 9Cr18MoV | 0.85～0.95 | ≤0.80 | ≤0.80 | ≤0.035 | ≤0.030 | 17.00～19.00 | 1.00～1.30 | 0.07～0.12 | |